Calcium Oxide Decomposed From Chicken’s and Goat’s Bones as Catalyst For Converting Discarded Cooking Oil to be Biodiesel

Calcium Oxide Decomposed From Chicken’s and Goat’s Bones as Catalyst For Converting Discarded Cooking Oil to be Biodiesel

Biodiesel; Discarded cooking oil; Calcium oxide; Chicken’s bone; Goat’s bone

Thermal decomposition of calcium oxide from chicken’s (Gallus gallus domesticus) and goat’s (Capra Hircus Aegragus) bones was prepared at temperature variations of 400, 500, 800, 900, 1000, and 1100 oC respectively. X-ray diffractometer (XRD), FT-IR and SEM were used for calcium oxide characterization. XRD diffraction pattern of the bone’s after thermal decomposition at 1100oC has similarity to the XRD standard diffraction pattern from Joint Committee on Powder Diffraction Standard (JCPDS). Diffractions of 2q values being used are 34.2o, 37.3o, 58.3o, 64.1o, and 67.3 o.  Ca-O presence in the samples was detected by FT-IR characterization at wavenumber of 354,90 cm-1. SEM profile show reducing size of bones after decomposition in both chicken’s and goat’s bones. Furthermore, the prepared calcium oxide was applied for biodiesel synthesis from discarded cooking oil through transesterification reaction. By applying the catalysts decomposed from chicken’s and goat’s bones, the biodiesel product showed characteristics as follows: biodiesel applied the chicken’s bone catalyst has fatty acid number of 0.56 mg/KOH, iod number of 22.41 g I2/100 g KOH, density of 0.88 g/cm3 and viscosity of 5.91 mm2/s, while biodiesel applied the goat’s bone catalyst has 0.56 mg/KOH, iod number of 21.57 g I2/100 g KOH, density of 0.88 g/cm3 and viscosity of 6.34 mm2/s. Those biodiesel’s characteristic values meet the National Standard of Indonesia (SNI) for biodiesel.

Lesbani, Aldes; Department of Chemistry, Faculty of Mathematic Natural Sciences, Sriwijaya University

Susi, Yosine

Verawaty, Marieska

Mohadi, Risfidian

Aceh International Journal of Science and Technology; Vol 4, No 1 (2015): January - April 2015

2088-9860

Graduate School of Syiah Kuala University

2015-01-22

Copyright (c) 2015 Aceh International Journal of Science and Technology

http://jurnal.unsyiah.ac.id/AIJST/article/view/2124/pdf_11

application/pdf

eng

info:eu-repo/semantics/article

info:eu-repo/semantics/publishedVersion

Peer-reviewed Article

http://jurnal.unsyiah.ac.id/AIJST/article/view/2124

10.13170/aijst.4.1.2124